Shaanxi Jude Steel Co., Ltd

 

The ASTM A249 TP304/304L Welded Steel Pipe is a seamless, austenitic stainless steel pipe designed for high-temperature and corrosive environments. It is made from high-grade stainless steel, which ensures it is highly resistant to corrosion, heat, and chemical damage. The pipes are machine-finished to a specified size, ensuring they meet strict dimensional and quality standards.

 

 

TP304: Carbon (C) content ≤0.08%, Silicon (Si) content ≤1.00%, Manganese (Mn) content ≤2.00%, Phosphorus (P) content ≤0.045%, Sulfur (S) content ≤0.030%, Chromium (Cr) content is 18.00 - 20.00%, Nickel (Ni) content is 8.00 - 11.00%.

 

TP304L: Carbon (C) content ≤0.035%, Silicon (Si) content ≤1.00%, Manganese (Mn) content ≤2.00%, Phosphorus (P) content ≤0.045%, Sulfur (S) content ≤0.030%, Chromium (Cr) content is 18.00 - 20.00%, Nickel (Ni) content is 8.00 - 13.00%. Compared with TP304, TP304L has a lower carbon content, which makes it less sensitive to intergranular corrosion during welding and has better welding performance and corrosion resistance.

 

 

Tensile strength: TP304 is generally above 515MPa, TP304L is slightly lower, usually above 485MPa.

 

Yield strength: TP304 has a yield strength of at least 205MPa, while TP304L has a yield strength of at least 170MPa.

 

Elongation: Both have good elongation, generally above 35%.

 

 

Chemical industry: Due to ASTM A249 TP304/304L Welded Steel Pipe good corrosion resistance, it can be used to transport various chemicals, acids, alkalis and other media, such as pipelines for manufacturing chemical equipment, linings of reactors, etc.

 

Food processing industry: It meets food hygiene standards and can be used for material conveying pipelines in food production, beverage processing and other processes, as well as parts of food processing equipment.

 

Pharmaceutical industry: It can be used to manufacture pipeline systems and containers in pharmaceutical production equipment to ensure the purity and safety of the pharmaceutical production process.

 

Construction industry: It is used in some architectural decorations and structures that require corrosion resistance and aesthetics, such as railings, handrails, and decorative pipes on the facades of buildings.

 

Energy industry: It is suitable for oil and natural gas pipelines, as well as related pipeline systems in energy facilities such as nuclear power plants.

 

Welding characteristics: The welding performance is good, but it is necessary to pay attention to controlling the welding parameters and processes during the welding process to avoid the occurrence of welding defects, such as thermal cracks, pores, etc. For ASTM A249 TP304/304L Welded Steel Pipe, due to its low carbon content, the intergranular corrosion tendency generated during welding is small, but appropriate welding process measures still need to be taken, such as using suitable welding materials and controlling welding heat input. Generally, no special heat treatment is required after welding, but if there are higher requirements for the performance of the welded joint, appropriate post-weld heat treatment, such as solution treatment, can be performed to improve the structure and performance of the welded joint.

 

Quality control: Strict ASTM A249 TP304/304L Welded Steel Pipe quality control standards must be followed during the production process, including inspection of raw materials, process control during production, and inspection of finished products. Raw materials must ensure that they meet the specified chemical composition and mechanical property requirements; welding process parameters, pipe diameter dimensional accuracy, wall thickness uniformity, etc. must be controlled during the production process; finished products must undergo appearance inspection, dimensional measurement, non-destructive testing (such as eddy current testing, ultrasonic testing, etc.) and mechanical property testing to ensure that product quality meets the requirements of ASTM A249 standards

 